ORAJET^® 3930
Photoluminescent

Three-layer moulded, light yellow, cadmium-free premium PVC film with glossy surface. Fulfils the requirements of DIN 67510. The afterglow effect is characterised by a particularly high initial brightness, immediately after switching off the stimulating light source. The excitation can be carried out as often as required without reducing the luminous properties of the film. Does not contain radioactive materials.

Product information

Technical properties

Resistance

Durability	5 Year(s)	with vertical outdoor weathering, central European normal climate; unprinted
Shelf Life	2 Year(s)	in original packaging, at 20 °C and 50 % relative humidity
Maximum shrinkage	Maximum shrinkage along: 0.2 mm Maximum shrinkage across : 0.2 mm	Bonded to steel \| FINAT TM 14
Elongation at break	Minimum elongation at break along: 100 % Minimum elongation at break across: 100 %	DIN EN ISO 527
Tensile strength	Minimum tensile strength along: 12 MPa Minimum tensile strength across: 10 MPa	EN ISO 527
Temperature resistance	Minimum temperature: -40 °C Maximum temperature: 100 °C	adhered on aluminium, central European normal climate

Adhesive properties

Adhesive power	18 N/25 mm	after 72 h, on stainless steel \| FINAT TM 1, average value
Adhesive	Permanent

Processing

Recommended printing procedure	Inkjet printing with solvent-based inks, Inkjet printing with UV inks, Inkjet printing with latex inks
Application temperature	Minimum temperature 8 °C

Product Construction

Liner	Liner: PE-coated paper on both sides, siliconised on one side Surface weight: 143 g/m²
Front material	Front material: Premium PVC film Manufacturing process: Moulded
Adhesive	Solvent-polyacrylate