ORACAL^® 8710
Dusted Glass Cal

Polymer PVC film for glass decoration. The reduced surface gloss of the film prevents unwanted reflections.

Product information

Technical properties

Resistance to cleaning agents	No change	adhered on glass, 8 h in detergent solution with 0.5 % household detergent at room temperature and at 65 °C
Durability	7 Year(s)	with professional processing, with vertical outdoor weathering, central European normal climate
Shelf Life	2 Year(s)	in original packaging, at 20 °C and 50 % relative humidity
Resistance to solvents and chemicals	Oils, Greases, Fuels, Aliphatic solvents, Weak acids, Salts and alkalis	at room temperature, 72 h after adhesion on aluminium, short-term
Maximum shrinkage	Maximum shrinkage along: 0.1 mm Maximum shrinkage across : 0 mm	adhered on glass \| FINAT TM 14
Elongation at break	Minimum elongation at break along: 130 % Minimum elongation at break across: 130 %	DIN EN ISO 527
Tensile strength	Minimum tensile strength along: 20 MPa Minimum tensile strength across: 20 MPa	EN ISO 527
Temperature resistance	Minimum temperature: -40 °C Maximum temperature: 90 °C	bonded to glass, normal Central European climate

Adhesive power	18 N/25 mm	adhered on glass, after 24 h \| Average value, FINAT TM 1
	16 N/25 mm	adhered on acrylic, after 24 h \| Average value, FINAT TM 1
Adhesive	Permanent

Processing

Application temperature	Minimum temperature 8 °C
Proposed application technology	Wet application

Product Construction

Front material	Thickness front material: 0.07 mm Front material: Polymer PVC film
Adhesive	Solvent-polyacrylate

Thickness	0.07 mm	Average value, without protective liner and adhesive

Dimensions

PDF, 54.97kB, 1 Page

PDF, 107.18kB, 3 Pages

PDF, 140.56kB, 1 Page